| Typical raffia, fiber/yarn applications include: Woven industrial fabric and bag Rope and cordage Woven carpet backing Woven geotextile fabrics Large parts Good resistance to gas fading&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Solvent resistance,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.906 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw D, 3.20 mm, injection molded | 70 | ASTM D2240 | |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 37.0 | MPa | ASTM D638 |
| Bending modulus | |||
| Secant, 3.20 mm, injection molded | 1590 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 31 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm, injection molded | 101 | ℃ | ASTM D648 |
| Notes |
|---|
| 1. May be used in contact with all types of foods at conditions of use A through H |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 2,0 in/min |
| 4. 0,051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |