| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | |||
| 23 ℃, 24 hours in water | 0.95 | % | ISO 62 |
| 23 ℃, saturated, in water | 1.4 | % | ISO 62 |
| 23 ° C/50% r. h, saturated | 2.20 | % | ISO 62 |
| Density | 1.36 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9600 | MPa | ISO 527-1/-2 |
| Tensile stress | |||
| Yield, 2 in/min | 175 | MPa | ASTM D638 |
| fracture | 175 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| Yield, 50 mm/min | 3.4 | % | ISO 527-1/-2 |
| fracture | 3.4 | % | ISO 527-1/-2 |
| elongation at break | |||
| 2 in/min | 3.5 | % | ASTM D638 |
| Bending modulus | |||
| 8700 | MPa | ISO 178 | |
| 8900 | MPa | ASTM D790 | |
| bending strength | 260 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23°C | 80 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23°C | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 216 | ℃ | ASTM D648 |
| 1.82 MPa | 210 | ℃ | ASTM D648 |
| Melting temperature | |||
| DSC (10°C/min) | 222 | ℃ | ISO 11357-1/-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1E+13 | IEC 62631-3-2 | |
| Volume resistivity | 1E+13 | IEC 62631–3-1 | |
| Compared to the leakage tracing index | 550 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 1.6 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80.0 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Temperature at the rear of the barrel | 230 – 235 | °C | |
| Temperature in the middle of the barrel | 235 – 240 | °C | |
| Front temperature of material barrel | 240 – 250 | °C | |
| Mold temperature | 60.0 – 80.0 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |