| About |
|---|
| Polypropylene Lumicene® M3382MZ produces thermoformed parts with superior clarity, gloss and excellent side wall stiffness. Lumicene® M3382MZ is ideal for deli containers, drinking cups, lids, domes and food service trays when high clarity (NX8000) and stiffness are important.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,Homopolymer |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.5 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 31.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 7.0 | % | ASTM D638 |
| Bending modulus | 1490 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 59 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 97.2 | ℃ | ASTM D648 |
| Melting temperature | 153 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 232 to 260 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |