Durethan® BKV 20 FN20 000000

About
Durethan® BKV 20 FN20 000000 (干燥 ) PA 6, 20 % glass fibers, injection molding, halogen free flame retardant&&Durethan® BKV 20 FN20 000000 PA 6, 20 % glass fibers, injection molding, halogen free flame retardant&&

Product Description
Supplier	LANXESS
Generic	PA6
Material Status	Commercial: Active
Features	Halogen free,Flame Characteristics,V-2
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.31	g/cm³	ISO 1183
Shrinkage rate			ISO 2577
TD：260℃，2.0 mm	0.70	%	ISO 2577
TD：120℃，2.0 mm，4 hrs	0.10	%	ISO 2577
MD：260℃，2.0 mm	0.60	%	ISO 2577
MD：120℃，2.0 mm，4 hrs	0.10	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	6100	MPa	ISO 527-1-2
tensile strength
Fracture, 23 ℃	100	MPa	ISO 527-2/5
Tensile strain
Fracture, 23 ℃	3.0	%	ISO 527-2/5
Bending modulus
23℃	6100	MPa	ISO 178-A
bending strength			ISO 178/A
3.50% strain, 23 ℃	165	MPa	ISO 178-A
23℃	170	MPa	ISO 178-A
Bending strain	4.5	%	ISO 178/A

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	< 10	kJ/m²	ISO 179/1eA
23℃	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	30	kJ/m²	ISO 179/1eU
23℃	35	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch			ISO 180/1A
-30℃	< 10	kJ/m²	ISO 180-1A
23℃	< 10	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam
23℃	30	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	185	℃	ISO 75-2/A
0.45 MPa, unannealed	215	℃	ISO 75-2/B
Vicat Softening Temp
B120	205	℃	ISO 306/B120
Ball pressure test
212℃	Pass		IEC 60695-10-2
Melting temperature	222	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD：23~55℃	9.0E-5	1/℃	ISO 11359-2
MD：23~55℃	4.0E-5	1/℃	ISO 11359-2

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	5.0E+14	ohms	IEC 60167
Volume resistivity
23℃	6.0E+15	ohms·cm	IEC 60093
Dielectric strength
23 ℃，1 mm	32	kV/mm	IEC 60243-1
Compared to the leakage tracing index	PLC 1		UL 746
Compared to the leakage tracing index
Solution A	525	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.75 mm	V-2		UL 94
1.50 mm	V-2		UL 94
3.00 mm	V-2		UL 94
Glowing wire flammability index			IEC 60695-2-12
0.75 mm	960	℃	IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire			IEC 60695-2-13
0.75 mm	775	℃	IEC 60695-2-13
1.5 mm	775	℃	IEC 60695-2-13
3 mm	775	℃	IEC 60695-2-13
Extreme oxygen index	27	%	ISO 4589-2

Supplementary information	Nominal value	Unit	Test method
ISO Shortname	PA 6, GFHR, 12-060, GF20		ISO 1874

Process Conditions
injection	Nominal value	Unit	Test method
Drying Temperature – Dry Air Dryer	80	°C
Drying Time – Dry Air Dryer	2.0 to 6.0	hr
Processing (melt) temperature	250 to 270	°C
Mold temperature	80 to 100	°C
Residual Moisture Content	0.030 to 0.070	%

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.