| BLUESTAR® PBT 403M-G30 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include: Flame Rated Flame Retardant Good Processability High Flow&& |
| Product Description | |
|---|---|
| Supplier | Zhonglan |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 to 1.63 | g/cm³ | ASTM D792 |
| Ash Content | 28.0 to 34.0 | ISO 3451 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 105 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.8 | % | ASTM D638 |
| Bending modulus | 8000 | MPa | ASTM D790 |
| bending strength | 165 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.50 | kJ/m² | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 55.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 200 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| In oil | 18 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 50 Hz | 3.40 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 0.020 | ASTM D150 | |
| 60 Hz | 0.020 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Nozzle temperature | 240 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Injection pressure | 70.0 to 120 | MPa | |
| Back pressure | 6.00 to 18.0 | MPa | |
| Screw speed | < 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.39 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |