| About |
|---|
| Versaflex™ OM 6160-9 is specifically designed to bond to a variety of standard and modified nylon materials, including those which are glass-filled, heat stabilized and/or impact modified. Excellent Surface Appearance Outstanding Adhesion in Both Two-Shot and Insert Molding Processes Soft, Rubbery Grip Very Easy to Process&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,Good bond,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds | 60 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 3.06 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 2.28 | MPa | ASTM D412 |
| 300% Strain, 73°F | 2.95 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 370 | % | ASTM D412 |
| tear strength | 24.5 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 31 | % | ASTM D395B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 38 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.7 to 2.1 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，11200 sec^-1 | 19.6 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 166 to 193 | °C | |
| Barrel middle temperature | 249 to 260 | °C | |
| Barrel front temperature | 254 to 277 | °C | |
| Nozzle temperature | 254 to 277 | °C | |
| Processing (melt) temperature | 260 to 277 | °C | |
| Mold temperature | 16 to 38 | °C | |
| Back pressure | 0.00 to 0.689 | MPa | |
| Screw speed | 75 to 175 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |