| About |
|---|
| ABS resin for injection into the natural color, general purpose, excellent mechanical and thermal properties. High impact resistance, indicated for cromation combined with high brightness and excellent low temperature performance, and good che&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,High impact resistance,Antifreeze,Solvent resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 160 | J/m | ASTM D256 |
| 0℃，3.2mm | 230 | J/m | ASTM D256 |
| 23℃，3.2mm | 310 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 91.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 101 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 41.0 | MPa | ASTM D638 |
| 3.20 mm | 40.0 | MPa | ASTM D638 |
| Bending modulus | 1960 | MPa | ASTM D790 |
| bending strength | 63.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 195 to 230 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Injection pressure | < 82.7 | MPa | |
| Back pressure | < 0.689 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |