| About |
|---|
| AS-SG401A63 is a glass fiber reinforced by PPS bassed PA66 aloy to provide excellent mechanical strength, toughness, and rigidity, along with excellent flow in thin-walled parts, low flash characteristics, and fast cycle times. It may be easily molded in conventional injection molding equipment utilizing water heated molds&& |
| Product Description | |
|---|---|
| Supplier | Sciengy |
| Generic | PPS+PA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High liquidity,Quick molding cycle |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.80 | % | |
| MD | 0.30 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 155 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 225 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| Dielectric constant | 4.00 | IEC 60250 | |
| Dissipation factor | 3.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 170 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 290 to 330 | °C | |
| Mold temperature | 120 to 160 | °C | |
| Injection pressure | 30.0 to 100 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |