| About |
|---|
| NORYL GTX964 is an unfilled impact modified material with optimised processability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Negative |
| Features | Excellent Processability,High impact resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，2.16 kg | 7.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.4 to 1.8 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 3.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 20 | kJ/m² | ISO 179/1eA |
| 23℃ | 45 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 20 | kJ/m² | ISO 180-1A |
| 23℃ | 50 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 175 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| A50 | 240 | ℃ | ISO 306/A50 |
| B50 | 175 | ℃ | ISO 306 |
| B120 | 180 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.23 | W/m/K | ISO 8302 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 80.0 | MPa | ISO 2039-1 |
| Tensile modulus | 2000 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 50.0 | MPa | ISO 527-2/50 |
| fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 50 | % | ISO 527-2/50 |
| Bending modulus | 1800 | MPa | ISO 178 |
| bending strength | 70.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 290 to 320 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |