| About |
|---|
| Very high impact ABS. Toughness/rigidity. Good fatigue resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Fatigue resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 28 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 370 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 27 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 31.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 80.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 81.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 98.0 | ℃ | ASTM D1525, ISO 306/B50 11 14 |
| B120 | 100 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 8.8E-5 | 1/℃ | |
| TD：-40~40℃ | 8.6E-5 | 1/℃ | |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 | |
| Tensile modulus | |||
| — | 2270 | MPa | ASTM D638 |
| — | 2270 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 44.0 | MPa | ASTM D638 |
| yield | 47.0 | MPa | ISO 527-2/50 |
| fracture | 33.0 | MPa | ASTM D638 |
| fracture | 34.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 2.1 | % | ASTM D638 |
| yield | 2.7 | % | ISO 527-2/50 |
| fracture | 26 | % | ASTM D638 |
| fracture | 17 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2340 | MPa | ASTM D790 |
| — | 2250 | MPa | ISO 178 |
| bending strength | |||
| — | 71.0 | MPa | ISO 178 |
| Yield, 50 mm span | 72.0 | MPa | ASTM D790 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| — | 1.05 | g/cm³ | ASTM D792 |
| — | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 3.7 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 14 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| Apparent viscosity of melt | |||
| 240℃，1000 sec^-1 | 245 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 to 93.3 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Recommended injection volume | 50 to 70 | % | |
| Barrel rear temperature | 188 to 210 | °C | |
| Barrel middle temperature | 204 to 227 | °C | |
| Barrel front temperature | 216 to 238 | °C | |
| Nozzle temperature | 218 to 260 | °C | |
| Processing (melt) temperature | 218 to 260 | °C | |
| Mold temperature | 48.9 to 71.1 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 11. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |