| About |
|---|
| Riblene FF 30 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 30 is characterised by a good melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FF 30 are easily heat shrinkable and characterised by good optical and mechanical properties. Main Application Riblene FF 30 is recommended for the production of shrink film for medium and light loads, for lamination film and for blend.&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Optical performance,Food contact compliance,High molecular weight,Good melt strength,Low density,Good thermal contraction |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 70 | µm | |
| film thickness | 30 to 120 µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 70 µ m, blow molded film | 180 | MPa | ISO 527-3 |
| 1% secant, TD, 70 µ m, blow molded film | 190 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 70 µ m, blow molded film | 10.0 | MPa | ISO 527-3 |
| TD, yield, 70 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 70 µ m, blow molded film | 22.0 | MPa | ISO 527-3 |
| TD, fracture, 70 µ m, blow molded film | 19.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 70 µ m, blow molded film | 380 | % | ISO 527-3 |
| TD, fracture, 70 µ m, blow molded film | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 70 µ m, blow molded film | 180 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：70.0 µm | 45.0 | kN/m | ISO 6383-2 |
| TD：70.0 µm | 60.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 95.0 | ℃ | ISO 306/A |
| Melting temperature | 113 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 70 µ m, blow molded film | 65 | ASTM D2457 | |
| Haze | |||
| 70.0 µ m, blow molded film | 8.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |