| ForTii®是突破性的高温聚酰胺，无卤阻燃牌号可用于电子、照明、汽车、白色家电、航空等行业中严苛的应用。&&ForTii® 的发展过程中，我们与行业尖端制造商以及连接器、插座等零部件厂商紧密合作，确保满足客户需求。&&高温尼龙系列产品众多，功能多样，可提供各种性能均衡的产品。 |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 4T |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Halogen free,Good stripping performance,Flame Characteristics,Lubricating,Heat Resistance, Good,Heat Stabilized |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.49 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.35 / * | % | ISO 294-4 |
| Shrinkage rate | |||
| MD | 1.05 / * | % | ISO 294-4 |
| Spiral flow length 1.0 mm 1000 bar | 55 / * | mm | – |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12500 / 12500 | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| -40℃ | 12500 / – | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 100℃ | 11600 / – | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 120℃ | 11200 / – | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 150℃ | 5300 / * | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 200℃ | 3740 / * | MPa | ISO 527-1-2 |
| Fracture stress | 240 / 220 | MPa | ISO 527-1/-2 |
| Fracture stress (-40 ° C) | 260 / – | MPa | ISO 527-1/-2 |
| Fracture stress (100 ° C) | 170 / – | MPa | ISO 527-1/-2 |
| Fracture stress (120 ° C) | 145 / – | MPa | ISO 527-1/-2 |
| Fracture stress (150 ° C) | 80 / * | MPa | ISO 527-1/-2 |
| Tensile stress (200 ° C) | 55 / * | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | 2.6 / 2.4 | % | ISO 527-1/2 |
| Fracture strain (-40 ° C) | 2.7 / – | % | ISO 527-1/-2 |
| Fracture strain (100 ° C) | 2.7 / – | % | ISO 527-1/-2 |
| Fracture strain (120 ° C) | 2.8 / – | % | ISO 527-1/-2 |
| Fracture strain (150 ° C) | 8 / * | % | ISO 527-1/-2 |
| Fracture strain (200 ° C) | 8 / * | % | ISO 527-1/-2 |
| Weld seam strength (thickness 1) | 90 / – | MPa | ISO 527-1/-2 |
| Elongation rate of weld seam (thickness 1) | 1 / – | % | ISO 527-1/-2 |
| Thickness testing | 4 / * | mm | ISO 527-1/-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 330 / * | ℃ | ISO 11357-1/-3 |
| Glass transition temperature DMTA (tan d) method | 145 / * | °C | ASTM D5026/D7028 |
| Hot deformation temperature | |||
| 1.8 MPa | 300 / * | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| TD | 0.15E-4 | /℃ | ISO 11359-1/-2 |
| Linear coefficient of thermal expansion | |||
| MD | 0.52E-4 | /℃ | ISO 11359-1/-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 / – | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |