NORYL GTX™ GTX840 resin

About
40% glass filled PPE+PA66 blend for automotive under-the-hood and FLEN applications&&

Product Description
SupplierSABIC
GenericPPO(PPE)+PS+PA
Material StatusCommercial: Negative
AvailabilitysNorth America
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.45g/cm³ASTM D792 , ISO 1183
Melt Volume Rate
220℃,5 kg10.0cm³/10minISO 1133
Shrinkage rate Internal Method
MD:3.2 mm0.24 to 0.27%Internal Method
TD:3.2 mm0.60 to 0.63%Internal Method
Water absorption rate 
Equilibrium, 23 ℃0.30%ASTM D570
Equilibrium, 23 ℃, 50% RH0.10%ISO 62

IMPACTNominal valueUnitTest method
Charpy Notched Impact Strength 
-30℃11kJ/m²ISO 179/2C
23℃11kJ/m²ISO 179/1eA
Impact strength of cantilever beam notch 
-30℃90J/mASTM D256
23℃94J/mASTM D256
-30℃11kJ/m²ISO 180-1A
23℃11kJ/m²ISO 180-1A

THERMALNominal valueUnitTest method
Hot deformation temperature 
0.45 MPa, unannealed, 6.4 mm260ASTM D648
0.45 MPa, unannealed, 64 mm span258ISO 75-2/Bf
1.8 MPa, unannealed, 6.4 mm247ASTM D648
1.8 MPa, unannealed, 64 mm span244ISO 75-2/Af
Vicat Softening Temp
B50246ISO 306/B50 , ISO 306/B120
B120246ISO 306/B50 , ISO 306/B120
Linear coefficient of thermal expansion ASTM E831
MD:-40~40℃1.6E-5 to 2.0E-51/℃ASTM E831
TD:-40~40℃9.0E-5 to 9.4E-51/℃ASTM E831

MECHANICALNominal valueUnitTest method
Rockwell hardness
R-level108 ASTM D785
Tensile modulus 
13500MPaASTM D638
13900MPaISO 527-1-2
tensile strength 
fracture178MPaASTM D638
fracture198MPaISO 527-2/5
Tensile strain 
fracture2.0%ASTM D638
fracture2.0%ISO 527-2/5
Bending modulus 
50 mm span11900MPaASTM D790
12300MPaISO 178
bending strength 
280MPaISO 178
Yield, 50 mm span249MPaASTM D790

Process Conditions
injectionNominal valueUnitTest method
Drying time, maximum8.0hr

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.20 in/min
3. Type I, 0.20 in/min
4. 0.051 in/min
5. 0.079 in/min
6. at Yield
7. 80*10*4 sp=62mm
8. 80*10*4 mm
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.