| About |
|---|
| Unreinforced Medium Viscosity Polybutylene Terephthalate Developed for Food Contact Applications&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Food contact compliance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2600 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 59.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | 45 | % | ISO 527-2 |
| bending strength | 85.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 60.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 180 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 115 | ℃ | ISO 75-2/B |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| Flammability level | |||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| Extreme oxygen index | 22 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | FMVSS 302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 34 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.6 | % | ISO 294-4 |
| MD | 1.6 | % | ISO 294-4 |
| Ejection temperature | 170 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Melt Temperature, Optimum | 250 | °C | |
| Mold temperature | 30 to 130 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Hold pressure | 60.0 | MPa | |
| Back pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Drying temperature | 110 to 130 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Melt temperature | 240 to 260 | °C | |
| Extrusion Melt Temperature, Optimum | 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |