INLUBE PPSCF30TF13SI2

About
30% CARBON FIBER REINFORCED, 15% PTFE/SILICONE LUBRICATED POLYPHENYLENE SULFIDE&&

Product Description
GenericPPS
Material StatusCommercial: Active
FeaturesLubricating
AvailabilitysNorth America
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.53g/cm³ASTM D792
Shrinkage rate
MD:3.2 mm0.050 to 0.20%ASTM D955
Water absorption rate
balance0.040%ASTM D570

MECHANICALNominal valueUnitTest method
tensile strength
fracture169MPaASTM D638
Tensile strain
fracture1.0 to 2.0%ASTM D638
Bending modulus20700MPaASTM D790

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch43J/mASTM D256

THERMALNominal valueUnitTest method
Hot deformation temperature
1.8 MPa, unannealed260ASTM D648

Electrical performanceNominal valueUnitTest method
Surface resistivity10 to 1.0E+2ohmsASTM D257

Process Conditions
injectionNominal valueUnitTest method
Drying temperature149°C
Drying time4.0hr
Processing (melt) temperature316 to 332°C
Mold temperature135 to 177°C
Back pressure0.345 to 0.689MPa
Screw speed40 to 70rpm
Vent depth7.6E-3 to 0.013mm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.