| Aegis® H35ZI is an unfilled, low viscosity, non-lubricated nylon 6 injection molding homopolymer exhibiting excellent melt flow properties for filling thin sections and reduced cycle times. It exhibits good strength, stiffness, and toughness as well as excellent heat, chemical and abrasion resistance.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low Viscosity,High Heat Resistance,Good wear resistance,Solvent resistance,Homopolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 235℃，1.0kg | 23 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.3 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 24hr | 1.6 | % | ASTM D570 |
| saturated | 9.5 | % | ASTM D570 |
| Balance, 50% RH | 2.7 | % | ASTM D570 |
| water content | < 0.10 | % | ASTM D6869 |
| Relative viscosity | |||
| @ 96% SAV | 2.34 | ||
| viscosity | |||
| FAV | 33.0 to 39.0 | ASTM D789 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 45 | J/m | ASTM D256 |
| 23℃ | 46 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 152 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 47.0 | ℃ | ASTM D648 |
| Melting temperature | 222 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 7.2E-5 | 1/℃ | ASTM E831 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| Tensile modulus | |||
| 23℃ | 2750 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 79.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 23 ℃ | 4.1 | % | ASTM D638 |
| Fracture, 23 ℃ | 75 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2470 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 96.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |