| SABIC® PP 90910 is a reactor-elastomer-modified material which offers a good cold impact resistance in combination with high flow. It is a highly attractive alternative to non-filled compounds and is typically used for painted car bumpers and exterior trim. SABIC® PP 90910 is a designated automotive grade.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Sprayable,Nucleation,low-temperature impact resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 22 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：24 hrs | 1.6 | % | Internal Method |
| 24 hrs | 1.6 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0 ℃, injection molding | 无断裂 | ISO 179/1eA | |
| 23 ℃, injection molding | 无断裂 | ISO 179/1eA | |
| Impact strength of cantilever beam notch | |||
| -20 ℃, injection molding | 200 | J/m | ASTM D256-A |
| 0 ℃, injection molding | 无断裂 | ASTM D256A , ISO 180/1A | |
| 23 ℃, injection molding | 无断裂 | ASTM D256A , ISO 180/1A | |
| -20 ℃, injection molding | 15 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| — | 125 | ℃ | ASTM D1525 4 , ISO 306/A120 4 |
| B120 | 49.0 | ℃ | ASTM D1525 5 , ISO 306/B120 5 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 50 | ISO 868 | |
| Tensile modulus | |||
| 1% cut, injection molding | 950 | MPa | ASTM D638 |
| injection molding | 850 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Yield, injection molding | 18.0 | MPa | ASTM D638 |
| Yield, injection molding | 18.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| Yield, injection molding | 8.0 | % | ASTM D638 |
| Yield, injection molding | 8.0 | % | ISO 527-2/1A/50 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. Rate B (120°C/h), Loading 1 (10 N) |
| 5. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |