| About |
|---|
| SAXALEN PPH329B20 is a 20% glass beads filled Polypropylene – Homopolymer intended for injection moulding. Low shrinkage, low warpage grade&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Low warping,Low contractility |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | |
| Melt Flow Rate | 10.0 | g/10min | ISO 1033 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 100 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 1600 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 40.0 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 1600 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 65.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 100 | ℃ | ISO 306 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.00 | kJ/m² | ISO 180-1A |
| -30℃ | 2.00 | kJ/m² | ISO 180-1A |
| Charpy Unnotch Impact strength | |||
| 23℃ | 35.0 | kJ/m² | ISO 179/1eU |
| -30℃ | 20.0 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 2.00 | kJ/m² | ISO 179/1eA |
| -30℃ | 1.00 | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | |||
| 23℃ | 27.0 | kJ/m² | ISO 180/1U |
| -30℃ | 13.0 | kJ/m² | ISO 180/1U |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Injection temperature | |||
| Rear barrel temperature | 220 -250 | °C | |
| Mold temperature | 40.0-70.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |