| About |
|---|
| PVC alloy for dark color capstock requiring premium weathering in both horizontal and vertical applications. May provide a wider processing window on traditional calibration tooling. Comes in low gloss. Best option for lower heat build-up in “jet black”.&& |
| Product Description | |
|---|---|
| Generic | PVC alloy |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Weather resistance is good,Low Gloss |
| Availabilitys | Asia Pacific,Europe,Africa & Middle East ,North America,Latin America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm, molded into shape | 27 | J/m | ASTM D256 |
| Falling impact resistance | ASTM D4226 | ||
| 23℃ | 59.2 | J/cm | ASTM D4226 |
| 23℃ | > 178 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 3.2 mm | 60.7 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 49.9 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 7.2E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 79 | ASTM D2240 | |
| Tensile modulus | 2230 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 31.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 55 | % | ASTM D638 |
| Bending modulus | 2340 | MPa | ASTM D790 |
| bending strength | |||
| yield | 79.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| Melt Temperature | 149 to 177 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. 2.0 in/min |
| 4. Procedure A, .125″ |
| 5. Procedure B, .125″ |
| 6. Conditioned at 50 deg.C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |