| About |
|---|
| EVALENE® PHT0171 is specifi cally developed for thermoforming and is intended for use in a broad range of extrusion applications requiring high impact strength and good stiffness. This resin is fully formulated with a nucleating agent resulting in improved cycle times as well as opportunities for enhanced end-product appearance. EVALENE® PHT0171 is ideal for containers requiring hot-fi ll and microwave compatibility. FEATURES High Izod Impact strength Good stiffness Good cycle times Good transparency Meets Philippine FDA food contact requirements Halal-certified TYPICAL APPLICATIONS Food Packaging Trays and Containers Drinking Cups Dunnage Trays Rigid Sheets&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Good Clarity,Good flexibility,High impact resistance,Nucleation,Food contact compliance,Homopolymer |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.7 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 18 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 120 | ℃ | ASTM D648 |
| Melting temperature | 162 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 103 | ASTM D785 | |
| Tensile modulus | |||
| 1% secant | 2410 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 38.0 | MPa | ASTM D638 |
| fracture | 18.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 13 | % | ASTM D638 |
| fracture | 65 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1470 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. 0.051 in/min |
| 5. Partial Break |
| 6. DSC, 10°C/min, 2nd heating |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |