| AIE PA6 50G6是一种聚酰胺6（尼龙6）材料,含有的填充物为30% 玻璃织物增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 AIE PA6 50G6的主要特性有: 阻燃/额定火焰 高流动性&& |
| Product Description | |
|---|---|
| Supplier | Asia International Enterprise (Hong Kong) |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High liquidity,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 1.7 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 180 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 8600 | MPa | ISO 178 |
| bending strength | 280 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 20 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 225 | ℃ | ISO 3146 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 50.0 to 100 | °C | |
| Injection pressure | 30.0 to 80.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |