| Clarity Medium Molecular Weight High Density Film Resin Characteristics Unique combination of high stiffness and clarity Good moisture barrier properties Good compatibility with LDPE and LLDPE Applications Cereal liners Paper overwrap Envelope windows Stand-up bags Release liners Coextruded films&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Moisture resistance,High density |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.959 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.80 | g/10min | |
| 190℃，21.6kg | 22 | g/10min | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | ASTM D882A | ||
| 1% secant, MD: 25 µ m | 1030 | MPa | |
| 2% secant, MD: 25 µ m | 689 | MPa | |
| 1% secant, TD: 25 µ m | 883 | MPa | |
| 2% secant, TD: 25 µ m | 703 | MPa | |
| tensile strength | ASTM D882A | ||
| MD, yield, 25 µ m | 31.0 | MPa | |
| TD, yield, 25 µ m | 31.0 | MPa | |
| MD, fracture, 25 µ m | 62.1 | MPa | |
| TD, fracture, 25 µ m | 24.1 | MPa | |
| Tensile strain | ASTM D882A | ||
| MD, fracture, 25 µ m | 600 | % | |
| TD, fracture, 25 µ m | 300 | % | |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：25 µm | 24 | g | |
| TD：25 µm | 390 | g | |
| Water vapor transmittance | |||
| 38℃，25 µm | 7.8 | g/m²/24 hr | ASTM E96 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 135 | ℃ | ASTM D3417 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 50 | ASTM D523 | |
| Haze | 15 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |