TOPAS® 5013F-04

About
Product Description TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS. Selected Applications Decorative film and sheet General packaging Food packaging Blown film Food contact Leading Attributes Gloss, hardness, chemical resistance, forming Easy or linear tear, heat resistance, hot fill, gloss Not manufactured with BPA, phthalates, or halogens High strength and high productivity Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 6013F-04 – high temperature grade with standard flow&&

About

Product Description TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS. Selected Applications Decorative film and sheet General packaging Food packaging Blown film Food contact Leading Attributes Gloss, hardness, chemical resistance, forming Easy or linear tear, heat resistance, hot fill, gloss Not manufactured with BPA, phthalates, or halogens High strength and high productivity Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 6013F-04 – high temperature grade with standard flow&&

Product Description
Supplier	Polyplastics
Generic	COC
Material Status	Commercial: Active
Features	Good Rigidity,Good Clarity,High purity,Good surface appearance,High liquidity,Halogen free,Food contact compliance,Moisture resistance,No BPA,Copolymer,Solvent resistance,Amorphous
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.02	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	< 0.10	g/10min	ISO 1133
230℃，2.16kg	8.0	g/10min	ISO 1133
Melt Volume Rate			ISO 1133
190℃，2.16 kg	< 0.100	cm³/10min	ISO 1133
230℃，2.16 kg	9.00	cm³/10min	ISO 1133
Water absorption rate
Saturation, 23 ℃	0.010	%	ISO 62

film	Nominal value	Unit	Test method
film thickness
test	70	µm
Tensile modulus			ISO 527-3/1
MD, 70 µ m, cast thin film	2600	MPa	ISO 527-3/1
TD, 70 µ m, cast thin film	2500	MPa	ISO 527-3/1
tensile strength			ISO 527-3/50
MD, fracture, 70 µ m, blow molded film	35.0	MPa	ISO 527-3/50
TD, fracture, 70 µ m, blow molded film	25.0	MPa	ISO 527-3/50
Tensile strain			ISO 527-3/50
MD, fracture, 70 µ m, cast thin film	1.4	%	ISO 527-3/50
TD, fracture, 70 µ m, cast thin film	1.1	%	ISO 527-3/50
Drop hammer impact
70 µ m, cast thin film	< 36	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD: 70 µ m, cast thin film	0.11	N	ISO 6383-2
TD: 70 µ m, cast thin film	0.11	N	ISO 6383-2
Oxygen permeability
23 ℃, 70 µ m, extruded film, 50% RH	26	cm³·mm/m²/atm/24 hr	ASTM D3985
Water vapor transmittance
70 µ m, 38 ℃, cast thin film, 90% RH	0.14	g·mm/m²/atm/24 hr	ASTM F1249

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	134	℃	ISO 11357-2

optical performance	Nominal value	Unit	Test method
gloss
60 °, 70.0 µ m, cast thin film	> 100		ISO 2813
Haze
70.0 µ m, cast thin film	< 1.0	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Extruder feed section	20 to 70	°C
Barrel 1 zone temperature	220 to 240	°C
Barrel 2 zone temperature	220 to 240	°C
Barrel 3 zone temperature	220 to 240	°C
Barrel 4 zone temperature	220 to 240	°C
Nozzle temperature	220 to 240	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.