| About |
|---|
| InnoPlus HD2200JP is high density polyethylene which can be processed in either injection or compression molding. This grade provides easy processing characteristics and exhibits excellent organoleptic properties Additive : non slip agent grade Typical Application : Caps and Closures for sparking and non sparking mineral/stilled water, tea and juice.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Food contact compliance,Good sensory characteristics.,High density |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.5 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, F50 | 4.00 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 49 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 3 |
| Melting peak temperature | 131 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression molding temperature | 140 to 165 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 66 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 30.4 | MPa | ASTM D638 |
| fracture | 20.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 1000 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1080 | MPa | ASTM D747 |
| Bending modulus | 1420 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 170 to 200 | °C | |
| Barrel middle temperature | 170 to 200 | °C | |
| Barrel front temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Complete Break |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |