| Jackdaw PLA HW10NT6624是一种聚乳酸 (PLA)产品,。 它可以通过挤出进行加工,在欧洲有供货。 主要特性为:环保/绿色。&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 35 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD | 0.40 | % | Internal Method |
| MD | 0.40 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ASTM D648，ISO 75-2/A |
| Melting temperature | 148 | ℃ | ISO 1218，ASTM D2117 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 75 | ASTM D2240 , ISO 868 | |
| Tensile modulus | 800 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| fracture | 16.0 | MPa | ISO 527-2 |
| — | 16.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 250 | % | ASTM D638 , ISO 527-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |