| About |
|---|
| CYCOLAC™ AMMG94F filament is a general purpose ABS product manufactured from CYCOLAC™ MG94 resin. It is available in black, white, and natural (unpigmented) colors. It provides a balance of properties suitable for a wide variety of applications and is UL94 HB compliant at 3.0 mm (Blue Cards are available on UL IQ Database). Nominal filament diameter is 1.79 mm ± 0.05 mm and it is available in a 1510 cc spool size.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| XY direction | 2070 | MPa | |
| XZ direction | 2130 | MPa | |
| ZX direction | 2030 | MPa | |
| tensile strength | |||
| XY direction, fracture | 26.0 | MPa | |
| XZ direction, fracture | 27.0 | MPa | |
| ZX direction, fracture | 26.0 | MPa | |
| Tensile strain | |||
| XY direction, fracture | 6.9 | % | |
| XZ direction, fracture | 5.9 | % | |
| ZX direction, fracture | 1.8 | % | |
| Bending modulus | |||
| XY direction | 2000 | MPa | |
| XZ direction | 2110 | MPa | |
| ZX direction | 1770 | MPa | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| XY direction, 23 ℃ | 160 | J/m | |
| XZ direction, 23 ℃ | 140 | J/m | |
| ZX direction, 23 ℃ | 59 | J/m | |
| Notched impact strength of cantilever beam | |||
| XY direction: 23 ℃ | 330 | J/m | |
| XZ direction: 23 ℃ | 320 | J/m | |
| ZX direction: 23 ℃ | 120 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| XY direction: 1.8 MPa, unannealed, 3.20 mm | 100 | ℃ | |
| XZ direction: 1.8 MPa, unannealed, 3.20 mm | 100 | ℃ | |
| ZX direction: 1.8 MPa, unannealed, 3.20 mm | 98.0 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD: XY direction | 7.6E-5 | 1/℃ | |
| MD: XZ direction | 7.7E-5 | 1/℃ | |
| MD: ZX direction | 8.2E-5 | 1/℃ | |
| TD: XY direction | 7.5E-5 | 1/℃ | |
| TD: XZ direction | 7.7E-5 | 1/℃ | |
| TD: ZX direction | 7.9E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| XZ direction | 1.3E+15 | ohms·cm | |
| XY direction | 4.1E+14 | ohms·cm | |
| Dielectric constant | |||
| XY direction: 100 MHz | 2.44 | ||
| XZ direction: 100 MHz | 2.46 | ||
| XZ direction: 500 MHz | 2.45 | ||
| XY direction: 500 MHz | 2.43 | ||
| XZ direction: 1.00 GHz | 2.43 | ||
| XY direction: 1.00 GHz | 2.41 | ||
| Dissipation factor | |||
| XZ direction: 100 MHz | 3.0E-3 | ||
| XY direction: 100 MHz | 3.0E-3 | ||
| XY direction: 500 MHz | 6.0E-3 | ||
| XZ direction: 500 MHz | 6.0E-3 | ||
| XY direction: 1.00 GHz | 5.0E-3 | ||
| XZ direction: 1.00 GHz | 5.0E-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| ZX direction, 3.00 mm | HB | ||
| XY direction, 3.00 mm | HB | ||
| XZ direction, 3.00 mm | HB |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. 0.051 in/min |
| 4. test coupons were printed using a Stratasys FORTUS† 900mc printer at high print density (94.9%) |
| 5. UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |