| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | LCP+PPS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good liquidity |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.10 to 0.20 | % | ASTM D955 |
| TD | 1.4 to 1.5 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 81.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.75 | % | ASTM D638 |
| Bending modulus | 12400 | MPa | ASTM D790 |
| bending strength | 116 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 22 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | > 245 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Volume resistivity | 10 to 1.0E+3 | ohms·cm | ASTM D257 |
| Charge Decay Time -（Mil-B-81705C），12% RH，5000kV to 50kV | 2 | msec | |
| Shielding effectiveness | |||
| 10GHz，3.2 mm | 61 | dB | |
| 1GHz，3.2 mm | 40 | dB | |
| 5GHz，3.2 mm | 55 | dB |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |