| PA610 15% carbon fiber reinforced injection moulding grade. Heat stabilized. Black colour. Suitable for parts and components requiring high mechanical properties. The presence of carbon fibers also provides higher electrical and thermal conductivity. This grade is partially renewably-sourced (60% of base polymer by weight).&& |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | Conductive,Renewable resources,Thermal conductivity,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 2.7 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 1.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11600 | MPa | |
| tensile strength | |||
| fracture | 180 | MPa | |
| Tensile strain | |||
| fracture | 4.0 | % | |
| Bending modulus | 9500 | MPa | |
| bending strength | 245 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 65 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 217 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+5 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | -20 | °C | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 4. 500V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |