| OREVAC® CA100 is a chemically functionalized polypropylene with a high content of maleic anhydride. Grafted maleic anhydride induces polarity to polypropylene and so outstanding adhesion properties on glass and natural fibers, and mineral fillers. Applications OREVAC® CA100 has been designed as coupling agent to develop a reliable bonding strength between PP or PA resins and glass fiber, mineral filler or natural fibers.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good bond |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，0.325kg | 10 | g/10min | ASTM D1238 |
| 190℃，0.325kg | 10 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, molded | 22.0 | MPa | ASTM D638 |
| Fracture, molded | 22.0 | MPa | ISO 527-2 |
| Yield, molding | 22.0 | MPa | ASTM D638 |
| Yield, molding | 22.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 12 | % | ISO 527-2 |
| Fracture, molded | 12 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 880 | MPa | ISO 178 |
| Compression Molding | 880 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 147 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | 147 | ℃ | ISO 306/A |
| Melting temperature | 167 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |