| About |
|---|
| Polyamide 6 elastomer modified, good impact resistance. Available: all colors, UV stabilized (L), release agent (W).&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Good stripping performance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 to 1.13 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 250℃，1.20kg | 15 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.1 to 1.6 | % | ASTM D955 |
| TD | 1.1 to 1.6 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 1.8 | % | ASTM D570，ISO 62 |
| saturated | 8.5 | % | ASTM D570 |
| Saturation, 23 ℃ | 8.5 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2750 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 100 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 2400 | MPa | ASTM D790 , ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | ASTM D256，ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179 , ASTM D256 | |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 75 | J/m | ASTM D256，ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ASTM D648，ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 195 | ℃ | ISO 306/B50 , ASTM D1525 3 |
| Melting temperature | 220 | ℃ | ASTM D211，ISO 121 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 5.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 2 mm | 18 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Extreme oxygen index | 23 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 80 to 90 | °C | |
| Pre-drying equipment | 80 to 100 | °C | |
| Drying time | |||
| — | 1.0 | hr | |
| Pre-drying equipment | 3.0 | hr | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 6x4x50 mm |
| 3. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |