| About |
|---|
| EVALENE ® PHJ1202 resin is intended for use in a broad spectrum of injection molding applications requiring excellent balance of processability, rigidity and toughness. This resin has been designed for molded products that demand the optimum combination of performance and economics. FEATURES Medium Flow Balanced mechanical properties Good impact/rigidity balance Good surface gloss Meets Philippine FDA food contact requirements Halal-certified TYPICAL APPLICATIONS Caps and Closures General-purpose Containers Housewares & Toys Rigid Packaging&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Quick molding cycle,Homopolymer |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 14 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 93.0 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 103 | ASTM D785 | |
| Tensile modulus | |||
| 1% secant | 1830 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 33.0 | MPa | ASTM D638 |
| fracture | 20.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 19 | % | ASTM D638 |
| fracture | 1100 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1120 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |