Leona™ 1502S

About
Leona™ 1502S is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 1502S include automotive, engineering/industrial parts, industrial applications and sheet. Characteristics include: Heat Resistant Heat Stabilizer High Molecular Weight High Strength&&

Product Description
Supplier	Asahi Kasei
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,High molecular weight,Heat Resistance, Good,Heat Stabilized
Availabilitys	Asia Pacific,North America,Europe,Africa & Middle East

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.14	g/cm³	ASTM D792
Molding shrinkage
Flowing flow	1.3-2.0	%	Internal Method
Water Absorption
Equilibrium equilibrium, 23 ℃, 50% r. h	2.5	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile Modulus
23 ℃, dry	2900	MPa	ISO 527
23 ℃, moist cond	1000	MPa	ISO 527
Tensile Stress
Yield yld, 23 ℃, dry dry	84	MPa	ISO 527
Yield yld, 23 ℃, wet cond	51	MPa	ISO 527
Dry	79	MPa	ASTM D638
Wet Cond	57	MPa	ASTM D638
Tensile Strain
Yield yld, 23 ℃, dry dry	4.5	%	ISO 527
Yield yld, 23 ℃, wet cond	26	%	ISO 527
Broken BRK, dry dry	80	%	ASTM D638
Broken BRK, wet Cond	270	%	ASTM D638
Broken BRK, 23 ℃, wetted Cond	>100	%	ISO 527
Flexural Modulus
Dry	2800	MPa	ASTM D790
Wet Cond	1200	MPa	ASTM D790
23 ℃, dry	2700	MPa	ISO 178
23 ℃, moist cond	900	MPa	ISO 178
Flexural Strength
Dry	118	MPa	ASTM D790
Wet Cond	54	MPa	ASTM D790
23 ℃, dry	110	MPa	ISO 178
23 ℃, moist cond	39	MPa	ISO 178
Taber Abrasion	5	mg	ASTM D1044
Rockwell hardness
M-grade, dry	80		ASTM D-785
M-grade, moist cond	55		ASTM D-785
R-grade, dry	120		ASTM D-785
R-grade, moist cond	105		ASTM D-785
M scale, dry dry	80		ISO 2039-2
M scale, wet cond	55		ISO 2039-2
R scale, dry dry	120		ISO 2039-2
R scale, wet cond	105		ISO 2039-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
Dry	5	kJ/m²	ISO 179
Wet Cond	30	kJ/m²	ISO 179
Charpy Unnotch Impact strength
Dry	NB		ISO 179
Wet Cond	NB		ISO 179
Izod Notched Impact strength
Dry	49	J/m	ISO 180/1A
Wet Cond	180	J/m	ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature HDT
0.45 MPa, unannealed	230	℃	ASTM D648
0.45 MPa, unannealed	195	℃	ISO 75-1/-2
1.8 MPa, unannealed	70	℃	ASTM D648
1.8 MPa, unannealed	65	℃	ISO 75-1/-2
Coeff. of linear thermal expansion	8E-5	cm/cm/℃	ASTM D696
Specific Heat	1670	J/kg/℃
Thermal conductivity	0.2	W/m/K

ELECTRICAL	Nominal value	Unit	Test method
Surface Resistivity	1E14	ohms	ASTM D257
Volume Resistance
	1E15	ohms·cm	ASTM D257
23℃	1E15	ohms·cm	IEC 60093
Dielectric Strength	20	kV/mm	ASTM D149
Compared Tracking Index	525	V	IEC 60112

Process Conditions
Injection Molding	Nominal value	Unit	Test method
Drying Temperature	80-90	℃
Drying Time	2-3	hr
Melt Temperature	270-290	℃
Mold Temperature	75-85	℃

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.