LEXAN™ LUX1832 resin

About
LEXAN™LUX1832树脂是支链聚碳酸酯树脂。是一种具有高机械，光学，电学和热性能的无定形紫外线稳定级别PC。具有抗冲击性，优异的尺寸稳定性，良好的加工性和清晰度。通过挤压吹塑加工。用于LED应用。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Excellent Processability,High impact resistance,Good Dimensional Stability
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, Type I, 50 mm/min	61	MPa	ASTM D638
Type I, 50 mm/min	63	MPa	ASTM D638
Tensile strain
Fracture, Type I, 50 mm/min	94	%	ASTM D638
Type I, 50 mm/min	7	%	ASTM D638
Tensile modulus
50 mm/min	2226.87	MPa	ASTM D638
bending strength
Yield, 1.30 mm/min, 50 mm span	100.062	MPa	ASTM D790
Bending modulus
1.3 mm / min，50mm跨距	2364.21	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	803.6	J/m	ASTM D256
Impact strength of cantilever beam notch
-30℃	117.6	J/m	ASTM D256
Instrument impact energy peak
23℃	652	cm-kgf	ASTM D 3763

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	145	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, unannealed, 3.2 mm	127	℃	ASTM D648
0.45 MPa, unannealed, 3.2 mm	141	℃	ASTM D648
Linear coefficient of thermal expansion
TD：-40~40℃	6.7E-05	1/℃	ASTM E831
MD：-40~40℃	6.6E-05	1/℃	ASTM E831

PHYSICAL	Nominal value	Unit	Test method
Density	1.2		ASTM D792
Shrinkage rate
MD：3.2 mm	0.6 – 0.9	%	Internal Method
Melt Flow Rate
300℃，1.20kg	3	g/10min	ASTM D1238

Process Conditions
Extrusion molding	Nominal value	Unit	Test method
Drying temperature	75 – 90	°C
Drying time	2 – 4	hrs
Minimum moisture content	0.04	%
Melt temperature	180 – 200	°C
Barrel – Zone 1 Temperature	165	°C
Barrel – Zone 2 Temperature	170	°C
Barrel – Zone 3 Temperature	175	°C
Barrel – Zone 4 Temperature	180	°C
Roll stack temperature – top	175 – 180	°C
Roll stack temperature – middle	175 – 180	°C
Roll stack temperature – bottom	175 – 180	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.