Safron® H106-02NSA

About
Safron® H106-02NSA Polypropylene Resin is a grade designed specifically for carbonated closure applications. The material is highly nucleated offering fast cycle times and also contains slip and antistatic additives. It exhibits a combination of high stiffness and toughness properties, as well as outstanding processing characteristics. Safron® H106-02NSA Polypropylene Resin may also be used for selected injection moulding applications other than closures. Typical Applications Carbonated closures Selected domestic and industrial applications&&

About

Safron® H106-02NSA Polypropylene Resin is a grade designed specifically for carbonated closure applications. The material is highly nucleated offering fast cycle times and also contains slip and antistatic additives. It exhibits a combination of high stiffness and toughness properties, as well as outstanding processing characteristics. Safron® H106-02NSA Polypropylene Resin may also be used for selected injection moulding applications other than closures. Typical Applications Carbonated closures Selected domestic and industrial applications&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Good flexibility,Smoothness,Nucleation,Quick molding cycle,Food contact compliance,Antistatic property,Homopolymer
Availabilitys	Africa & Middle East
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	2.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, injection molding	35.0	MPa	ISO 527-2
Tensile strain
Yield, injection molding	7.0	%	ISO 527-2
Bending modulus
injection molding	1480	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
0 ℃, injection molding	2.2	kJ/m²	ISO 179
23 ℃, injection molding	6.0	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	83.0	℃	ISO 75-2/B
1.8 MPa, unannealed	55.0	℃	ISO 75-2/A

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Barrel rear temperature	190	°C
Barrel middle temperature	230 to 260	°C
Barrel front temperature	270	°C
Nozzle temperature	240	°C
Barrel 1 zone temperature	200	°C
Barrel 2 zone temperature	200 to 270	°C
Barrel 3 zone temperature	220 to 300	°C
Barrel 4 zone temperature	240 to 300	°C
Nozzle temperature	250	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.