| Advanced-PP 1101P is a propylene homopolymer fibre grade characterized by medium flowability, medium molecular weight distribution and medium crystallinity providing excellent and consistent process and product behavior. Advanced-PP 1101P is particularly suitable for the production of staple fibre, bulked continuous filaments (BCF), continuous filaments (CF). The product is comprised of an advanced pheno free stabilizer package providing superior gasfading resistance and inherent basic UV-stability. Application BCF / CF of higher dtex and relatively lower line speed than standard BCF grades. Regulatory Information: The Grade Advanced-PP 1101P and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011 (and its amendments). Specific information is available upon request.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Hypocrystalline,Moderate liquidity,Solvent resistance,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，50% RH | 0.10 | % | ISO 62 |
| 23℃，24hr | 0.10 | % | ISO 62 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 26 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 35 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | >=10 | % | ISO 527-2 |
| Fracture, 23 ℃ | 50 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 1550 | MPa | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 85 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| A50 | 92 | ℃ | ISO 306/A50 |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-4 | 1/℃ | ISO 11359-2 |
| melting point | 163 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | >=1.0E+15 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+14 | Ω.cm | IEC 60093 |
| Insulation strength | 140 | KV/mm | IEC 60243-1 |
| Dielectric constant | 2.3 | 1 MHz | IEC 60250 |
| Dissipation factor | 0.00020 | 1 MHz | IEC 60250 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 105 | kJ/m² | ISO 179/1eU |
| -30℃ | 15 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/1eA |
| -30℃ | 1.5 | kJ/m² | ISO 179/1eA |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60-90 | °C | |
| Drying time | 2.0-6.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 200-260 | °C | |
| Barrel middle temperature | 210-270 | °C | |
| Barrel front temperature | 220-280 | °C | |
| Nozzle temperature | 230-290 | °C | |
| Mold temperature | 20-90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |