| Hostacom HBC 386L G81523 is a 40% talc filled PP homopolymer, with low flowability, high stiffness and good LTHS (long term heat stability). Suitable for visible parts without long term steam, hot water and detergent exposure. Product is UL listed. Please contact Basell for shrinkage recommendations. The product is available as a customized color matched, pellet form. This grade is delivered in G81523 color version. This grade is not intended for medical, pharmaceutical, food, drinking water and all applications not listed in the supported list. For more information please contact our sales representatives.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat aging resistance,Low liquidity,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，5.0kg | 10 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，5 kg | 10.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 4000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 31.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 3.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 4300 | MPa | ISO 178-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| 0℃ | 15 | kJ/m² | ISO 179/1eU |
| 23℃ | 25 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 122 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 74.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 95.0 | ℃ | ISO 306/B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |