| About |
|---|
| SABIC® PPcompound 7715 is a mineral filled modified polypropylene. This material combines high scratch resistance with a high stiffness, medium impact and good flow. This material has a broad processing window combined with good esthical performance. Typical applications include esthetical automotive interior parts such as door panels and interior trim. SABIC® PPcompound 7715 is a designated automotive grade.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good liquidity,High scratch resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 24 hrs | 0.95 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, injection molding | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -40 ℃, injection molding | 40 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/4A | ||
| -20 ℃, injection molding | 3.0 | kJ/m² | |
| 0 ℃, injection molding | 5.0 | kJ/m² | |
| 23 ℃, injection molding | 8.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 115 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 135 | ℃ | ISO 306/A |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| -30 to 30 ℃ | 7.0E-5 | cm/cm/℃ | |
| 23 to 80 ℃ | 1.0E-4 | cm/cm/℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 65 | ISO 868 | |
| tensile strength | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, injection molding | 26.0 | MPa | |
| Fracture, 3.20 mm, injection molded | 18.0 | MPa | |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 60 | % | ISO 527-2/5/50 |
| Bending modulus | |||
| injection molding | 1800 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method I (3 point load) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |