| PC2502NH is balance peformance and 1.6mm V-0 flame retardant non-halogenand PC resin. It has excellent UV stability. PC2502NH is mainly used in monitor housings,LCD, household electric product, etc.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 62.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 100 | % | ASTM D638 |
| Bending modulus | 2100 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 580 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Back pressure | 0.200 to 0.800 | MPa | |
| Screw speed | 20 to 80 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |