| About |
|---|
| Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins. This resin also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties. Smoke: Radel® R-5000 CL 301 Amber: Radel® R-5000 NT Blue: Radel® R-5000 TR BU391&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Material Status | Commercial: Active |
| Features | Gamma radiation,High Heat Resistance,Radiation disinfection,Heat Stabilized,Solvent resistance,Flame Characteristics,Good Electrical Properties,Ultra high toughness,Good Dimensional Stability,Hydrolysis stability,Radioactive,Steam sterilized,High ESCR,Ethylene oxide disinfection,Good heat aging resistance,E-beam disinfection,Good disinfection,Resistance to the steam,Biocompatible,Heat sterilization,Resistance to detergents,V-0,High pressure disinfection,Acidproof,Alkali resistant |
| Availabilitys | Latin America,Europe,North America,Asia Pacific |
| Process Methods | Injection Molding,Film extrusion,Extrusion,Thermo forming,Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 365℃，5.0kg | 14 to 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 | % | ASTM D955 |
| Water Absorption | |||
| Balancing Equilibrium | 1.1 | % | ASTM D570 |
| 24hr | 0.37 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.18 mm | 2340 | MPa | ASTM D638 |
| Tensile Strength | |||
| 3.18 mm | 69.6 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK, 3.18 mm | 60 to 120 | % | ASTM D638 |
| Yield yld, 3.18 mm | 7.2 | % | ASTM D638 |
| Flexural Modulus | |||
| 3.17 mm | 2410 | MPa | ASTM D790 |
| Flexural Strength | |||
| 5% strain, 3.18 mm | 91.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 3.2mm | 690 | J/m | ASTM D256 |
| Tensile Impact Strength | |||
| 3.18 mm | 399 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed, 3.2 mm | 207 | ℃ | ASTM D648 |
| Glass Transition Temperature | 220 | ℃ | ASTM E1356 |
| Coeff. of linear thermal expansion | |||
| MD：3.2 mm | 5.6E-5 | 1/℃ | ASTM D696 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 0.0254 mm | > 200 | kV/mm | ASTM D149 |
| 3.18 mm | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 3.18 mm，60 Hz | 3.44 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.76 mm | V-0 | UL 94 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive Index | 1.672 | ASTM D542 |
| Additional Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Steam Sterilization（w/ Morpholine） | > 1000 | Cycles |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 171 | °C | |
| Drying Time | 4.0 | hr | |
| Barrel Zone 1 Temperature | 338 to 388 | °C | |
| Barrel Zone 2 Temperature | 338 to 388 | °C | |
| Barrel Zone 3 Temperature | 338 to 388 | °C | |
| Barrel Zone 4 Temperature | 338 to 388 | °C | |
| Barrel Zone 5 Temperature | 338 to 388 | °C | |
| Adapter Temperature | 327 to 371 | °C | |
| Melt Temperature | 343 to 399 | °C | |
| Die Temperature | 327 to 371 | °C | |
| Drying Temperature | 149 | °C | |
| Drying Time | 2.5 | hr | |
| Melt Temperature | 360 to 391 | °C | |
| Mold Temperature | 138 to 163 | °C | |
| Screw Compression Ratio | 2.2:1.0 | ||
| Notes |
|---|
| 1. NSF STD-51 compliant for NT only. |
| 2. Tested at 82 °C (180 °F) (Commercial Hot) |
| 3. Typical properties: these are not to be construed as specifications. |
| 4. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 5. Cycles passed without cracking, crazing, or rupture. Steam Autoclave Conditions: – Temperature: 270°F (132°C) – Time: 30 minutes/cycle – Steam Pressure: 27 psig (0.19 MPa) – Stress Level: 1000 psi (7.0 MPa) in flexure – Additive: Morpholine at 50 ppm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |