Vipel® K010-TBE-30

About
AOC’s Vipel K010-TB series are promoted bisphenol A, epoxy-based vinyl ester resins dissolved in styrene and methyl methacrylate. Flame and smoke resistance is obtained by incorporating at least 60 parts of alumina trihydrate per 100 parts of resin. Vipel K010-TB series are ideally suited for use in hand lay-up, spray-up and filament winding processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. BENEFITS Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts. Vipel K010-TB series is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Vipel K010-TB series resins are highly resistant to several chemical environments.&&

About

AOC’s Vipel K010-TB series are promoted bisphenol A, epoxy-based vinyl ester resins dissolved in styrene and methyl methacrylate. Flame and smoke resistance is obtained by incorporating at least 60 parts of alumina trihydrate per 100 parts of resin. Vipel K010-TB series are ideally suited for use in hand lay-up, spray-up and filament winding processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. BENEFITS Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts. Vipel K010-TB series is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Vipel K010-TB series resins are highly resistant to several chemical environments.&&

Product Description
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Good flexibility,Corrosion Resistant,Flame Characteristics,High Heat Resistance,Good tear strength,Solvent resistance,High ESCR
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3600	MPa	ASTM D638
tensile strength	89.6	MPa	ASTM D638
Tensile strain
fracture	4.0	%	ASTM D638
Bending modulus	3700	MPa	ASTM D790
bending strength	155	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	110	℃	ASTM D648

Supplementary information	Nominal value	Unit
Gel to Peak	11.0	min
HAP Content	42	%
exothermic peak	178	℃
Thixotropic index	1.30

Uncured Properties	Nominal value	Unit
Density	1.04	g/cm³
viscosity
Brookfield LV	0.23	Pa·s
Gelation time	30	min

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.