| About |
|---|
| Product Description | |
|---|---|
| Supplier | NHU |
| Material Status | Commercial: Negative |
| Features | Solvent resistance,Flame Characteristics,High Viscosity |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1360 | kg/m³ | ISO 1183 |
| Forming shrinkage rate | |||
| TD | 1.2 | % | |
| MD | 1.8 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.02 | % | ISO 62 |
| Ash Content | |||
| 750℃ | 0.1 | wt% | ISO 3451-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.3 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 50 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 105 | ℃ | ISO 75-1,-2 |
| 8.0 MPa | 95 | ℃ | ISO 75-1,-2 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：-50 ℃ | 5.8E-5 | 1/℃ | ISO 11359-2 |
| MD：150 ℃ | 5.8E-5 | 1/℃ | ISO 11359-2 |
| TD：-50 ℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：150 ℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Glass transition temperature | |||
| 10℃/min | 90 | ℃ | ISO 11357-2 |
| melting point | |||
| 10℃/min | 280 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohm | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohm·cm | IEC 60093 |
| Voltage resistance (insulation failure strength) | 18 | kV/mm | IEC 60243-1 |
| Relative dielectric constant | |||
| 23℃，1MHz | 3.2 | IEC 60250 | |
| Dissipation factor | |||
| 23℃，1MHz | 0.004 | IEC 60250 | |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 90 | MPa | ISO 527-1,2 |
| Tensile modulus | |||
| 23℃ | 3500 | MPa | ISO 527-1,2 |
| elongation at break | |||
| 23℃ | 3.5 | % | ISO 527-1,2 |
| bending strength | |||
| 23℃ | 150 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 3800 | MPa | ISO 178 |
| Rockwell hardness | |||
| 23℃ | 90 | M Scale | ISO 2039-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |