| J50-2000-119 is a narrow molecular weight high density polyethylene copolymer intended for applications requiring a glossy finish and reasonably good impact strength and rigidity. It is characterized by a high melt index which allows easy processing of medium to thin walled articles. This material meets the Food and Drug Administration requirements of 21 CFR 177.1520.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,High impact resistance,Food contact compliance,Weight distribution,Copolymer,High density |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ASTM D4883 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, F50 | 1.80 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 66 | ASTM D2240 | |
| tensile strength | |||
| fracture | 26.8 | MPa | ASTM D638 |
| yield | 27.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 230 | % | ASTM D638 |
| yield | 9.1 | % | ASTM D638 |
| Bending modulus | |||
| tangent | 1230 | MPa | ASTM D790-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 28 | J/m | ASTM D256 |
| Area | 2.77 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 72.2 | ℃ | ASTM D648 |
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |