| About |
|---|
| Polifil ® TPOT-2024UV is a UV stabilized injection molding grade of compounded TPO utilizing metallocine catalyst technology. This product is intended for applications requiring outstanding impact properties at both ambient and low temperatures needing UV stabilization. The talc filler provides controlled shrinkage and reduced part warpage. Typical applications include automotive interior kick panels, bumper and fascia components, recreational vehicle cowls, and lawn and garden machinery guards. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations to meet your application requirements.&& |
| Product Description | |
|---|---|
| Generic | PO增强 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low warping,High impact resistance,Low contractility,low-temperature impact resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 24 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.50 mm | 0.090 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 5.00 | kJ/m² | |
| 23℃ | > 22.0 | kJ/m² | |
| Drop hammer impact | |||
| -20℃，12.7 mm | > 15.0 | J | |
| 23℃，12.7 mm | > 35.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 62.0 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 67 | ASTM D955 | |
| tensile strength | |||
| Yield, 23 ℃ | 26.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 23 ℃ | 6.0 | % | |
| Fracture, 23 ℃ | > 100 | % | |
| Bending modulus | |||
| Tangent, 23 ℃ | 2300 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 33.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 99 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Barrel rear temperature | 199 to 210 | °C | |
| Barrel middle temperature | 210 to 216 | °C | |
| Barrel front temperature | 216 to 221 | °C | |
| Nozzle temperature | 221 to 227 | °C | |
| Processing (melt) temperature | 204 to 232 | °C | |
| Mold temperature | 10 to 60 | °C | |
| Injection speed | 快速 | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |