| About |
|---|
| LNP* THERMOCOMP* UF13HWZ270 is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized, Non-Brominated & Non-Chlorinated Flame Retardant. Also known as: LNP* THERMOCOMP* Compound UF-1003 HW Z270 Product reorder name: UF0037W&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Heat Stabilized,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.33 | g/cm³ | ASTM D792 |
| — | 1.34 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 0.50 to 0.90 | % | ASTM D955 |
| TD：24 hrs | 1.5 to 1.9 | % | ASTM D955 |
| TD：24 hrs | 1.5 to 1.9 | % | ISO 294-4 |
| MD：24 hrs | 0.50 to 0.90 | % | ISO 294-4 |
| Water absorption rate | |||
| 24hr，50% RH | 0.30 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 8480 | MPa | ASTM D638 |
| — | 8300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 113 | MPa | ASTM D638 |
| yield | 106 | MPa | ISO 527-2 |
| fracture | 113 | MPa | ASTM D638 |
| fracture | 106 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 2.3 | % | ASTM D638 |
| yield | 2.1 | % | ISO 527-2 |
| fracture | 2.3 | % | ASTM D638 |
| fracture | 2.1 | % | ISO 527-2 |
| Bending modulus | |||
| — | 7580 | MPa | ASTM D790 |
| — | 6300 | MPa | ISO 178 |
| bending strength | |||
| — | 179 | MPa | ASTM D790 |
| — | 174 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 43 | J/m | ASTM D256 |
| 23℃ | 4.4 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 340 | J/m | ASTM D4812 |
| 23℃ | 21 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 6.20 | J | ASTM D3763 |
| — | 1.50 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 271 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 270 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM E831, ISO 11359-2 | ||
| MD：-40~40℃ | 3.8E-5 | 1/℃ | |
| TD：-40~40℃ | 5.2E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |