| About |
|---|
| Polyether block amide Pebax® HD 5513 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide. Added to PA6, Pebax® HD 5513 SP 01 resin enhances the properties of PA6, especially at low temperatures and low humidity content, at the same time maintaining the transparency of the nylon film and improving its soft touch. This SP grade has been developed to be heat and UV resistant. Note that this grade was formerly named Pebax® MP 1878 SP 01 resin.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12弹性体 |
| Material Status | Commercial: Active |
| Features | Smoothness |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.3 | % | ISO 62 |
| 23℃，24hr | 6.7 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 58 | ISO 868 | |
| Shore D, 15 seconds | 54 | ISO 868 | |
| tensile strength | |||
| fracture | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 500 | % | ISO 527-2 |
| Bending modulus | 180 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40℃ | 34 | kJ/m² | ISO 179 |
| 23℃ | No Break | ISO 179 | |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -40℃ | No Break | ISO 179 | |
| 23℃ | No Break | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 169 | ℃ | ISO 306 |
| Melting temperature | 195 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 25 to 60 | °C | |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Melt temperature | 220 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |