| Novalloy-B B5706 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product filled with 30% glass fiber. It can be processed by coating or injection molding and is available in North America. Applications of Novalloy-B B5706 include electrical/electronic applications, business/office goods, coating applications and housings. Characteristics include: Flame Rated Chemical Resistant Wear Resistant Flame Retardant Good Adhesion&& |
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | ABS+PBT |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good Dimensional Stability,High elastic,Good liquidity,Flame Characteristics,High Heat Resistance,Good bond,Good wear resistance,Grease resistance,Solvent resistance,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 123 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.2 | % | ASTM D638 |
| Bending modulus | 9510 | MPa | ASTM D790 |
| bending strength | |||
| yield | 176 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 210 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 200 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 20 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 100 Hz | 3.90 | ASTM D150 | |
| Dissipation factor | |||
| 100 Hz | 3.0E-3 | ASTM D150 | |
| Arc resistance | |||
| 3.18 mm | 71.0 | sec | ASTM D495 |
| Compared to the resistance to leakage and marking index | |||
| 3.18 mm | 250 | V | UL 746 |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.59 mm | 101 | UL 746 | |
| 3.18 mm | 69.0 | UL 746 | |
| High voltage arc marking rate (HVTR) (3.18 mm) | 40.6 | mm/min | UL 746 |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.59 mm | 27 | sec | UL 746 |
| 3.18 mm | 53 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 121 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Processing (melt) temperature | 241 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.483 to 1.45 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |