| About |
|---|
| RP340R is a high melt flow rate random copolymer. It features high transparency and gloss combined with good flowability, good balance of rigidity/impact and very low odor and flavor transfer. Applications: Injection of high transparency parts. Processing: Injection Molding&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Good liquidity,Low odor,Random copolymer |
| Availabilitys | Latin America,Europe |
| Process Methods | Injection Stretch Blow Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 |
| Density | 0.902 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | ASTM D1238 |
| 230℃，2.16kg | 25 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 3.0 | kJ/m² | ISO 180 |
| 23 ℃, injection molding | 50 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, injection molded | 78.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 78.0 | ℃ | ISO 75-2/B |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 1000 µ m, injection molding | 17 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, injection molding | 31.0 | MPa | ISO 527-2 |
| Yield, injection molding | 30.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, injection molding | 14 | % | ASTM D638 |
| Yield, injection molding | 12 | % | ISO 527-2 |
| Bending modulus | |||
| 1% cut, injection molding | 1000 | MPa | ASTM D790 |
| 1% cut, injection molding | 1100 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 82 | ISO 2039-2 | |
| R-level | 84 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |