| About |
|---|
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Nucleation,Quick molding cycle,Good stripping performance,Copolymer,Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 70 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1 mm/min | 1.500 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 50 mm/min | 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 50 mm/min | 4.0 | % | ISO 527-2 |
| Bending modulus | 1.500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 3.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 102 | ℃ | ISO 75-2 |
| Dissolution temperature | |||
| DSC | 165 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 250 | °C | |
| Mold temperature | 10 to 15 | °C | |
| Injection speed | Medium to high | ||
| Maintaining pressure | 20.0 to 50.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |