| Clariant Nylon 6/6 PA-111G43是一种聚酰胺66（尼龙66）材料,含有的填充物为43% 玻璃纤维增强材料。 该产品在北美洲有供货,加工方式为:注射成型。 Clariant Nylon 6/6 PA-111G43的主要特性有: 阻燃/额定火焰 高强度 良好的刚度 典型应用领域包括: 电线电缆 工程/工业配件 工业应用 汽车行业&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.40 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 257 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 266 | ℃ | ASTM D648 |
| Melting temperature | 255 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.3E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 22 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 207 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 11000 | MPa | ASTM D790 |
| bending strength | 283 | MPa | ASTM D790 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 97 | ASTM D785 | |
| R-level | 121 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 266 to 293 | °C | |
| Barrel middle temperature | 266 to 293 | °C | |
| Barrel front temperature | 266 to 293 | °C | |
| Processing (melt) temperature | 266 to 288 | °C | |
| Melt temperature (target) | 274 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |