| About |
|---|
| 40% Glass Reinforced, Low Flash, Excellent Mold Release&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good stripping performance,Low flash |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.50 | % | |
| MD | 0.20 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 11 | kJ/m² | |
| 23℃ | 11 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 62 | kJ/m² | |
| 23℃ | 60 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -40℃ | 12 | kJ/m² | |
| 23℃ | 12 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 55 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 265 | ℃ | ISO 75-2/A |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.5E-5 | 1/℃ | ISO 11359-2 |
| TD | 4.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 31 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.40 mm | V-0 | ||
| 1.6 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 100 | ||
| R-level | 120 | ||
| Tensile modulus | |||
| — | 15000 | MPa | |
| 120℃ | 9500 | MPa | |
| 160℃ | 5300 | MPa | |
| 200℃ | 4100 | MPa | |
| tensile strength | |||
| fracture | 205 | MPa | |
| Fracture, 120 ℃ | 100 | MPa | |
| Fracture, 160 ℃ | 65.0 | MPa | |
| Fracture, 200 ℃ | 50.0 | MPa | |
| Tensile strain | |||
| fracture | 2.1 | % | |
| Fracture, 120 ℃ | 2.9 | % | |
| Fracture, 160 ℃ | 3.8 | % | |
| Fracture, 200 ℃ | 3.9 | % | |
| Bending modulus | 14000 | MPa | ISO 178 |
| bending strength | 280 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. above Tg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |